I-Resin SZUV-T1150-ukumelana nokushisa okuphezulu
Isingeniso Esijwayelekile
Izici:
I-SZUV -T1150 iyinhlaka ye-SL ephuzi enokusebenza okushisayo okungenakuqhathaniswa. Iyakwazi ukumelana namazinga okushisa angaphezu kuka-200℃ ngesikhathi esifushane kanye no-120℃ ngesikhathi eside. Idizayinelwe ukuphatha izinhlobo eziningi zezinga lokushisa eliphezulu kanye nezinhlelo zokusebenza zokuhlola ezimbi.
Izici Ezijwayelekile
Amandla Aphakeme kanye Nokumelana Okuhle
I-SZUV-T1150 ingakwazi ukumisa umswakama, amanzi nezincibilikisi ezifana nophethiloli, uketshezi lokudlulisa, uwoyela kanye nokupholisa. Ngokumelana nokushisa okungenakuqhathaniswa, kufanelekile ukugeleza, i-HVAC, ukukhanyisa, ithuluzi, ukubumba kanye nezicelo zokuhlola umhubhe womoya.
Yakha Ngokushesha futhi Uthuthukise Ngokushesha
Ngokunikeza okukhiphayo okusheshayo nezingxenye ezinobuso obushelelezi, obuphatheka kalula, i-SZUV-T1150 ingakwazi ukuqedela iphrojekthi yakho kusukela ekudwebeni kuya ezingxenyeni zokuhlola ngesikhathi esifushane.
Uhlelo lokusebenza olujwayelekile
-Ukuhlolwa kwengxenye engaphansi kwe-hood
-Ukushisa okuphezulu kwe-RTV ukubumba
-Ukuhlolwa komhubhe womoya
-Ukuhlolwa kwezinto zokukhanyisa
-Inhlanganisela ye-autoclave tooling
Ukuhlolwa kwengxenye ye-HVAC
-Yenza ukuhlolwa okuhlukahlukene
- I-Orthodontics
Amacala ohlelo
Imfundo
Izibungu Ezandla
Izingxenye ze-Auto
Idizayini yokupakisha
I-Art Design
Ezokwelapha
?
| Ukubukeka | mhlophe |
| Ukuminyana | 1.13g/cm3@25 ℃ |
| I-Viscosity | 430~510 cps @ 27 ℃ |
| Dp | 0.155 mm |
| Ec | 7.3 mJ/cm2 |
| Ugqinsi lwesendlalelo sokwakha | 0.05 ~ 0.12mm |
?
| Isilinganiso | Indlela Yokuhlola | Inani | |
| Imizuzu engama-90 yokwelapha ngemuva kwe-UV | Imizuzu engama-90 ye-UV +2 amahora@160℃ emva kokwelashwa okushisayo | ||
| Ukuqina, Shore D | I-ASTM D 2240 | 88 | 92 |
| Flexural modulus, Mpa | I-ASTM D790 | 2776-3284 | 3601-3728 |
| Amandla e-Flexural, Mpa | I-ASTM D790 | 63-84 | 92-105 |
| I-tensile modulus, i-MPa | I-ASTM D638 | 2942-3233 | 3581-3878 |
| Amandla aqinile, i-MPa | I-ASTM D638 | 60-71 | 55-65 |
| Ukwandisa ngesikhathi sekhefu | I-ASTM D638 | 4-7% | 4-6% |
| Amandla omthelela, i-notched lzod, J/m | I-ASTM D 256 | 12-23 | 11-19 |
| Izinga lokushisa lokuphambuka kokushisa, ℃ | I-ASTM D 648 @66PSI | 91 | 108 |
| Ukuguqulwa kwengilazi, Tg, ℃ | DMA, E'peak | 120 | 132 |
| I-coefficient yokunwetshwa kwe-thermal, E6/℃ | I-TMA (T | 78 | 85 |
| I-Thermal conductivity, W/m.℃ | ? | 0.179 | ? |
| Ukuminyana | ? | 1.26 | ? |
| Ukumuncwa kwamanzi | I-ASTM D 570-98 | 0.48% | 0.45% |
?
?
?
?
?
?
?
?
?
?
?
?
?