I-Resin-SZUV-S9006-ukuqina okuphezulu
Intshayelelo ye-3D yoShicilelo lweMathiriyeli
Iimpawu
I-SZUV-S9006?
INGCACISO YEMVELISO
I-SZUV-S9006 yi-ABS efana ne-SL resin enayoubunzima obuphezuluIimbonakalo. Yenzelwe abashicileli bemeko eqinileyo yeSLA. I-SZUV-S9006 ingasetyenziswa kwiipatheni eziphambili, iimodeli zengqikelelo, iinxalenye zendibano kunye neeprototypes ezisebenzayo kushishino lweemoto, lwezonyango kunye nolwe-elektroniki lwabathengi. Izahlulo zokuqina kwesakhiwo kunye ne-SZUV-S9006 ingaphezulu kwe-6.5months.
?
OKUQHELEKILEYOIIMBONAKALO
-I-liquid resin's viscosity ephakathi, kulula ukuyiphinda kwakhona, kulula ukucoca iindawo kunye noomatshini
-Amandla aphuculweyo agciniwe, imilinganiselo ephuculweyo yokugcinwa kwamalungu akwimeko yokufuma
-Kufuneka ugqibezele kancinci
-Ubomi beshelufu ende kumatshini
-Phantsiukufinyela emazantsi?
?
OKUQHELEKILEYOIINZUZO
-Udinga ixesha elincinci lokugqiba, kulula ukunyanga emva kokunyanga
-I-Bulid echanekileyo kunye neendawo eziphezulu ezinzima kunye nozinzo oluphuculweyo lwe-dimensional
-Umgangatho ophezulu wokulawula iindawo zokukhupha i-vacuum
-I-low shrink kunye nokumelana kakuhle nokutyheli
-Umbala omhlophe omangalisayo
-Ogqwesileyo machinable SLA imathiriyeli?
Qaphela: ukushisa kwe-szuv-s9006 akufanele kube phezulu kakhulu. Nceda uyisebenzise ngaphantsi kwe-25℃. Ukufuma okunxulumeneyo kokusetyenziswa kunye nokugcinwa kufuneka kube ngaphantsi kwe-38RH%.
?
Iimeko zesicelo
EZINYE ZEPROJEKTHI ZAM
Imfundo
Izandla zokubumba
Amacandelo Auto
Uyilo lokuPakisha
Uyilo lobuGcisa
Ezonyango
?
?Iinkcazelo Ngeempawu (ulwelo)
| Imbonakalo | Mhlophe |
| Ukuxinana | 1.11-~1.15g/cm3@ 25 ℃ |
| Viscosity | 230 ~ 290cps @ 26 ℃ |
| Dp | 0.13~0.145 mm |
| Ec | 9.5 ~ 10.5 mJ/cm2 |
| Ubungqingqwa bomaleko wokwakha | 0.05~0.12mm |
?
Iipropati zoomatshini (Emva Kokunyanga)
| UMLINGANISO? | INDLELA YOVAVANYO? | VALUE |
| Imizuzu engama-90 ye-UV emva kokunyanga | ||
| Ubunzima, Unxweme D | I-ASTM D 2240 | 75-85 |
| Flexural modulus, Mpa | I-ASTM D 790 | 2,592-2,675 |
| Amandla e-Flexural, uMpa | I-ASTM D 790 | 63-70 |
| Imodyuli yokuqina, iMPa | I-ASTM D 638 | 2,489-2,595 |
| Amandla okuqina, MPa | I-ASTM D 638 | 36-53 |
| Ukwandisa ngexesha lekhefu | I-ASTM D 638 | 15-25% |
| Umlinganiselo wePoisson | I-ASTM D 638 | 0.4-0.44 |
| Amandla empembelelo inotshi Izod, J/m | I-ASTM D 256 | 45-70 |
| Ubushushu bokutshintsha ubushushu, ℃ | I-ASTM D 648 @66PSI | 38-50 |
| Utshintsho lweglasi,Tg | DMA, E”incopho | 40-54 |
| I-Coefficient yokwanda kwe-thermal | I-TMA(T | 90~102*E-6 |
| Ubuninzi, g/cm3 | ? | 1.12-1.18 |
| Dielectric Constant60 Hz | I-ASTM D 150-98 | 4.2-5.0 |
| I-Dielectric Constant 1 kHz | I-ASTM D 150-98 | 3.3-4.2 |
| Dielectric Constant1 MHz | I-ASTM D 150-98 | 3.2-4.0 |
| I-Dielectric Amandla kV/mm | I-ASTM D 1549-97a | 12.8-16.1 |
?